Thin-coated fire pattern vibration and wear-resistant combination Thin coating wire drawing vibration wear-resistant combination 3D laser carving combination Narrow-side vibration and wear-resistant combination Cosmetic PP material real plating combination Cosmetics ABS/PC material real plating combination

3C vibration wear-resistant combination recommendation

Cosmetic combination recommendation

Cosmetic PP material real plating combination Cosmetics ABS/PC material real plating combination

Classic plus color two-coating real plating combination recommendation

Classic plus color two-coating real plating combination recommendation Imitating anodizing effect (three-stage) Imitating anodizing effect (integrated type) No-bottom process Thin coating process Narrow side vibration and wear resistance

Homepage

Products

CASE

3C vibration wear-resistant combination recommendation

3D laser carving combination

1/1

Number of views:

1000

3D laser carving combination

Number of views:

1000

Category

3C vibration wear-resistant combination recommendation

Quantity



产品描述

3D laser carving combination

Coating combination

Color paint: H-2XXX (film thickness: 8-10µm; curing conditions: 75℃×10-15min )

Primer: ZD-3D309 (film thickness: 25-30µm; IR conditions: 55-60℃×5min; UV energy: 800~1000mj/cm2)

Intermediate coating: UV-203Z-37 (film thickness: 3~7µm; IR conditions: 65-70℃×5min; UV energy: 600~800mj/cm2)

Top paint: ZD-3M320 (film thickness: 30~35µm; IR conditions: 65-70℃×5min; UV energy: 800~1000mj/cm2)

Combined performance (refer to Huawei and Lenovo standards)

Serial number	Test items	Test conditions	Test results
1	Adhesion (one hundred grids)	One hundred grid method, spacing 1mm, 3M600# tape	≥4B
2	RCA abrasion resistance test	175g force	≥300 times
3	Alcohol resistance test	99.5% alcohol, 500g/300 times	No obvious fading or exposed substrate
4	Pencil hardness test	Mitsubishi pencil, 1000g force (ABS/PC material)	≥2H
5	Boiled test	80℃×30min or 100℃×10min	No obvious change,≥4B
6	Alternating heat and humidity	25℃-55℃×95%RH×72 hr	No obvious change, ≥4B
7	Temperature shock	70℃×2 hr /-40℃×2 hr 5 cycles	No obvious change,≥4B
8	Cosmetic resistance test	Vaseline 55℃×95%RH×48 hr	No obvious change, ≥4B
9	Hand sweat resistance test	pH=4.7/ pH=8.8 35℃×93%RH×48 hr	No obvious change,≥3B
10	Salt spray test	35℃×5%NaCl×48 hr	No obvious change, ≥4B
11	UV ultraviolet light irradiation test	60℃×4 hr(UV)/50℃×4 hr 12 cycles, 340nm wavelength	No obvious change,≥4B
12	Vibration and wear resistance	2hr	Level 2 and above

Thin coating wire drawing vibration wear-resistant combination

Narrow-side vibration and wear-resistant combination

Contact

Hipro Polymer Materials(Jiangsu)Co.,Ltd.
Address: NORTH INDUSTRIAL DISTRICT (NANCAO VILLIAGE),WANSHI TOWN,WUXI, YIXING, JIANGSU, CHINA
Sales Line：0510-87855326
Fax：0510-87855629
Technical Line：0510-87856185
Dr. Office：0510-87856290
Website：www.hiprocoating.com